Bayblend® 2953
(PC+ABS)-Blend; Vicat/B 120 temperature = 113°C; for electroplating applications
i
Market Switch
Selection will influence the results you get.
About
Product Types
- PC+ABS blend
Material
- Plastics
- Electroplating grade
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 240 - 270 | |
| Barrel Temperatures - Middle | - | °C | 235 - 245 | |
| Barrel Temperatures - Nozzle | - | °C | 265 - 275 | |
| Barrel Temperatures - Rear | - | °C | 230 - 240 | |
| Dry Air Drying Temperature | - | °C | 80 | |
| Dry Air Drying Time | - | h | 4 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 260 - 280 | |
| Moisture Content max. (%) | - | % | <= 0,02 | |
| Mold Temperatures | - | °C | 70 - 90 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 270 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 110 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 90 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 113 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 108 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2200 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 5.6 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 65 |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 46 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 35 |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 47 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2100 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 3.6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 44 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 14 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1110 |