Desmodur® CQ ultra Z 4470 MPA/X
Aliphatic polyisocyanate (IPDI trimer), using alternative feedstocks attributed via mass balance (ISCC PLUS certified). As the hardener component for lightfast polyurethane coating systems and as an additive resin for alkyd spray coatings.
i
市场转换
选择会影响你得到的结果。
关于
材料类型
- PIC
- IPDI
- 脂肪族聚异氰酸酯
- 交联剂
- 聚异氰酸酯
- 固化剂
- 聚异氰脲酯
- 异氰酸酯
材料
- 涂料、油漆和油墨
- 坚硬, 耐气候, 快速固化, 溶剂型, 超低单体
一般特征
Aliphatic polyisocyanate (IPDI trimer), using alternative feedstocks attributed via mass balance (ISCC PLUS certified).
As the hardener component for lightfast polyurethane coating systems and as an additive resin for alkyd spray coatings.
As the hardener component for lightfast polyurethane coating systems and as an additive resin for alkyd spray coatings.
储存条件
- Storage in original sealed Covestro container.
- Recommended storage temperature: 0 - 30 °C.
- Protect from moisture, heat and foreign material.
General information: The product is sensitive to moisture. Storage at higher temperatures will result in increase of color and viscosity. Storage at significant lower temperatures will result in solidification. This solidification is reversible by briefly heating the product without adversely affecting the quality of the product.
- Recommended storage temperature: 0 - 30 °C.
- Protect from moisture, heat and foreign material.
General information: The product is sensitive to moisture. Storage at higher temperatures will result in increase of color and viscosity. Storage at significant lower temperatures will result in solidification. This solidification is reversible by briefly heating the product without adversely affecting the quality of the product.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性特征
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Flash point | DIN 53 213/1 | °C | approx. 40 |
| Density at 20 °C | DIN EN ISO 2811 | g/ml | approx. 1.08 |
| Viscosity at 25 °C | M014-ISO 3219/A.3 | mPa*s | approx. 1,350 |
| Alternative carbon share 1 (bio-circular attributed) | calculated | % | 50 |
| ^1 carbon not originating from primary fossil sources expressed as percentage of the total carbon. | |||
| Alternative raw material share ^2 (bio-circular attributed) | calculated | wt.-% | 38 |
| ^2 elements not originating from primary fossil sources expressed as percentage of the total mass. | |||
| Equivalent weight | approx. 360 |
命名属性规范
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Viscosity at 23 °C | M014-ISO 3219/A.3 | mPa*s | 1,500 ± 500 |
| Color value (Hazen) | M017-EN 1557 | ≤ 60 | |
| NCO content | M105-ISO 11909 | % | 11.9 ± 0.4 |
| Monomeric IPDI | M106-ISO 10283 | % | < 0.1 |
| Non-volatile content (0.2 g/1 h/120 °C) | M020-ISO 3251 | % | 70 ± 2 |