Anionic high-molecular-weight polyurethane dispersion. Using renewable feedstock attributed via mass-balance (ISCC PLUS certified).
Dispercoll® CQ U 56 is a raw material for the formulation of thermally activated adhesives for use in, for example, the automotive, furniture, shoe and construction industries. Dispercoll® CQ U 56 is particularly well suited for applications with low thermal activation temperatures and is therefore particularly well suited for use on temperature-sensitive substrates.
Dispercoll® CQ U 56 is a raw material for the formulation of thermally activated adhesives for use in, for example, the automotive, furniture, shoe and construction industries. Dispercoll® CQ U 56 is particularly well suited for applications with low thermal activation temperatures and is therefore particularly well suited for use on temperature-sensitive substrates.
Lagerungsbedingungen
- Storage in original sealed Covestro containers.
- Recommended storage temperature: 5 - 23 °C, temperatures higher than
30 °C should be avoided.
- Protect from direct sunlight, frost, heat and foreign material.
General information: The product is sensitive to frost. Freezing can damage the product irreversibly. Prolonged storage at higher temperatures may affect the product properties and possibly resulting in sedimentation or coagulation.
Containers must be kept sealed and protected from direct sunlight as otherwise the evaporation of water will result in the formation of a non-redispersible polymer film.
Contamination with certain bacteria, fungi or algae may render the product unusable.
- Recommended storage temperature: 5 - 23 °C, temperatures higher than
30 °C should be avoided.
- Protect from direct sunlight, frost, heat and foreign material.
General information: The product is sensitive to frost. Freezing can damage the product irreversibly. Prolonged storage at higher temperatures may affect the product properties and possibly resulting in sedimentation or coagulation.
Containers must be kept sealed and protected from direct sunlight as otherwise the evaporation of water will result in the formation of a non-redispersible polymer film.
Contamination with certain bacteria, fungi or algae may render the product unusable.
Probenahme
Keine Daten verfügbar
Verpackungsart
Keine Daten verfügbar
Technische Eigenschaften & Datenblätter
Genannte Eigenschaften Merkmale
| Name der Eigenschaft | Prüfverfahren | Einheit | Wert |
|---|---|---|---|
| 1 not originating from primaryfossilsources | |||
| Alternative raw material 11bio-circular, attributed, without water | calculated | % by wt. | approx. 80.8 |
| Alternative raw material 11bio-circular, attributed | calculated | wt.-% | approx. 40.4 |
| Alternative carbon share 11bio-circular, attributed | calculated | % | approx. 86 |
| Density at 20 °C | DIN 51 757 | g/cm3 | approx. 1.1 |
| Minimum film-forming temperature | DIN ISO 2115 | °C | approx. 5 |
Genannte Eigenschaften Spezifikation
| Name der Eigenschaft | Prüfverfahren | Einheit | Wert |
|---|---|---|---|
| Viscosity at 23 °C,spindle L 2 / 30 rpm | DIN EN ISO 2555 | mPa*s | 50 - 900 |
| pH-value | DIN ISO 976 | 6.0 - 9.0 | |
| Non-volatile content (1g / 1h / 125 °C) | DIN EN ISO 3251 | % | 49 - 51 |