Aqueous colloidal dispersion of a 2-chlorobutadiene polymer with a high rate of crystallisation.
Dispercoll® C 84 is suitable for the formulation of aqueous adhesives for use in the footwear, construction, furniture, mattress and automotive industries.
Dispercoll® C 84 is suitable for the formulation of aqueous adhesives for use in the footwear, construction, furniture, mattress and automotive industries.
储存条件
- Storage in original sealed Covestro container.
- Recommended storage temperature: 10 - 25 °C.
- Protect from frost, heat and foreign material.
General information: This product is sensitive to frost, and must be protected from cold. Frozen product is irreversibly damaged. Containers must be kept sealed as otherwise the evaporation of water will result in the formation of a non-redispersible film. Due to the process, the product can tend toward subsequent creaming. This manifests in the form of a very thin, brown layer which after some time becomes visible on the surface of the product. Prior homogenization of the product using a suitable stirrer is recommended each time product is removed from the container.
- Recommended storage temperature: 10 - 25 °C.
- Protect from frost, heat and foreign material.
General information: This product is sensitive to frost, and must be protected from cold. Frozen product is irreversibly damaged. Containers must be kept sealed as otherwise the evaporation of water will result in the formation of a non-redispersible film. Due to the process, the product can tend toward subsequent creaming. This manifests in the form of a very thin, brown layer which after some time becomes visible on the surface of the product. Prior homogenization of the product using a suitable stirrer is recommended each time product is removed from the container.
样品
无可用数据
包装类型
220 or 1,000 l Schütz disposable container, tank truck
技术属性和数据表
命名属性特征
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| pH | DIN ISO 976 | approx. 13 | |
| Minimum film-forming temperature | DIN 53 787 | °C | approx. 5 |
| Apparent viscosityby the Brookfield Test method (LV / Sp2 / 60 rpm / 25°C) | DIN EN ISO 2555 | mPa*s | approx. 100 |
| Density | DIN 53 757 | g/cm3 | approx. 1.12 |
| Crystallization (relative classification acc. to Shore A hardness) | high | ||
| Gel content | Bayer method | low |
命名属性规范
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Non-volatile matter (2 g / 105 °C / 3 h) | DIN EN ISO 3251 | % | 55 ± 0.5 |