Baybond PU 403 is an anionic/non-ionic crosslinking polyester urethane polymer.
It is used as the film-forming component in glass fiber sizes.
It is used as the film-forming component in glass fiber sizes.
储存条件
Baybond PU 403 should be stored in tightly sealed original containers and protected from freezing, heat, and foreign materials. The product cannot be used if it has been frozen. Recommended storage temperature is 5º-30ºC.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性特征
属性名称 | 测试方法 | 单位 | 数值 |
---|---|---|---|
Elongation at break | % | 1,000 | |
Average particle size | nm | 200 - 400 | |
Tg | -47 | ||
100% Modulus | N/mm² | 3.4 | |
Tensile strength | N/mm² | 38 | |
Density at 20°C | g/ml | approx. 1.0 |
命名属性规范
属性名称 | 测试方法 | 单位 | 数值 |
---|---|---|---|
Particle size distribution Dv 0.5 | µm | ≤ 0.3 | |
Viscosity at 23ºC / 30 rpm / Sp. L-2 | mPa.s | < 250 | |
pH value at 20^oC (supply form) | 6.0 - 8.0 | ||
Particle size distribution Dv 0.9 | µm | ≤ 0.5 | |
Non-volatile content (0.9-1.1g/1h/125^oC, convection oven) | % | 38.0 - 40.0 |