The system is composed of the polyol Baynat® 2505 Acoustic and the Baynat® 0759 BX isocyanate, this system to be reacted is used for the production of rigid polyurethane foam in blocks with approximate density of 22 kg/m3.
The rigid thermoformable foam of Baynat® 2505 acoustic has a excellent dimensional stability properties, homogeneous and consistent cell structure as well as a high content of open cell that gives the foam excellent acoustic properties.
Baynat® foam is used mainly in sandwich constructions, in comination with layers of fiber covers and decorative material, for the manufacture of automotive awnings providing excellent characteristics to the final piece.
The rigid thermoformable foam of Baynat® 2505 acoustic has a excellent dimensional stability properties, homogeneous and consistent cell structure as well as a high content of open cell that gives the foam excellent acoustic properties.
Baynat® foam is used mainly in sandwich constructions, in comination with layers of fiber covers and decorative material, for the manufacture of automotive awnings providing excellent characteristics to the final piece.
Lagerungsbedingungen
The Baynat® 2505 Acoustic component B is slightly hygroscopic (can absorb water), so the containers must be hermetically sealed to prevent the passage of moisture, or foreign materials that may affect the performance of the material in a negative way. The masimum recommended temperature for storage is 50 °C (122 °F). The material in the containers must be stirred previously for 2 hours before use.
Isocyanate component A Baynat® 0759 BX isocyanate must be stored in hermetically sealed containers and protected from moisture and foreign materials, which may adversaly affect the process. Storage temperatures should be maintained at 21 °C to 30 °C (70°F to 86°F).
Isocyanate component A Baynat® 0759 BX isocyanate must be stored in hermetically sealed containers and protected from moisture and foreign materials, which may adversaly affect the process. Storage temperatures should be maintained at 21 °C to 30 °C (70°F to 86°F).
Probenahme
Keine Daten verfügbar
Verpackungsart
Keine Daten verfügbar
Technische Eigenschaften & Datenblätter
Genannte Eigenschaften Merkmale
| Name der Eigenschaft | Prüfverfahren | Einheit | Wert |
|---|---|---|---|
| Cream Time | sec | approx. 47 | |
| Mix Ratio by Weigh polyol/isocyanate | 100/160 | ||
| Material Temperature | °C | 25 ± 3 | |
| Free Rise Density | kg/m^3 | approx. 23.50 | |
| Rise Time | sec | approx. 314 | |
| Mold Temperature | Room temperature |
Genannte Eigenschaften Spezifikation
| Name der Eigenschaft | Prüfverfahren | Einheit | Wert |
|---|---|---|---|
| Water Content | % by wt. | approx. 4.7 | |
| ISOCYANATE | |||
| Dynamic Viscosity 25 °C | mPa.s | approx. 620 | |
| Specific Gravity 25 °C | approx. 1.04 | ||
| Dynamic Viscosity 25 °C | mPa·s | approx. 35.0 | |
| Appearance | Dark brown liquid | ||
| POLYOL | |||
| POLYOL | |||
| Appearance | Dark brown liquid | ||
| Specific Gravity 25 °C | approx. 1.219 | ||
| ISOCYANATE | |||
| Appearance | Black liquid | ||
| Appearance | Black liquid | ||
| Specific Gravity 25 °C | approx. 1.04 | ||
| NCO Content | % by wt. | approx. 32.5 | |
| NCO Content | % by wt. | approx. 32.5 | |
| Dynamic Viscosity 25 °C | mPa·s | approx. 35.0 | |
| Dynamic Viscosity 25 °C | mPa.s | approx. 620 | |
| No. OH | mg KOH/g | approx. 380 | |
| Specific Gravity 25 °C | approx. 1.219 | ||
| Water Content | % by wt. | approx. 4.7 | |
| No. OH | mg KOH/g | approx. 380 |