Bayflex® 5253 is a moldable microcellular polyurethane foam, designed for high production molded gasket applications such as radial seal filters.
储存条件
Avoid moisture contamination during storage, handling, and processing. For both components, pad containers with either nitrogen or dry air (desiccant cartridge or air dryer at -40°F dew point).
Store poly component B from 18 °C to 30 °C (65°F to 85°F). Mix poly component to a homogenous state before use and before removing any material from container.
For optimum shelf life, the recommended storage temperature for the isocyanate component is 20 °C to 35 °C (68°F to 95°F). Do not expose isocyanate component to lower temperatures – freezing may occur.
Store poly component B from 18 °C to 30 °C (65°F to 85°F). Mix poly component to a homogenous state before use and before removing any material from container.
For optimum shelf life, the recommended storage temperature for the isocyanate component is 20 °C to 35 °C (68°F to 95°F). Do not expose isocyanate component to lower temperatures – freezing may occur.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性特征
属性名称 | 测试方法 | 单位 | 数值 |
---|---|---|---|
Rise Time | seg | 78 ± 4 | |
Free Rise Density | kg/m^3 | 255 | |
Cream Time | seg | 26 ± 3 | |
Material Temperature | °C | 30 - 40 | |
Mix Ratio by Weigh polyol/isocyanate | 100/48 | ||
Mold Temperature | °C | 53 ± 5 |
命名属性规范
属性名称 | 测试方法 | 单位 | 数值 |
---|---|---|---|
Specific Gravity | approx. 1.05 | ||
Appearance | Black liquid | ||
No. OH | mg KOH/g | 138 | |
Water Content | wt. % | max. 0.3 | |
POLYOL | |||
Dynamic Viscosity 25 °C | mPa.s | 1200 |
下载
-
技术数据表
-
安全数据表无可用直接下载,请访问 www.productsafetyfirst.covestro.com