Addigy® LPU Flex 341-10 IM
Clear aliphatic polyether urethane acrylate resin specifically developed for 3D printing applications requiring high mechanical flexibility. By using it as a primary component in 3D printing formulations, the mechanical properties of the final printed parts can tuned in a wide range to meet the required specifications. This versatile resin is compatible with a variety of reactive thinners, mixable with other Addigy® LPU products, and can be used in 1- or 2-component based formulations in combination with isocyanate reactive compounds.
i
市场转换
选择会影响你得到的结果。
关于
材料类型
- 预聚物
- 聚氨酯树脂
- 预聚物
材料
- 3D打印
- 可与多种稀释剂相容
- 涂料、油漆和油墨
- 柔韧
一般特征
Clear aliphatic polyether urethane acrylate resin specifically developed for 3D printing applications requiring high mechanical flexibility.
By using it as a primary component in 3D printing formulations, the mechanical properties of the final printed parts can tuned in a wide range to meet the required specifications.
This versatile resin is compatible with a variety of reactive thinners, mixable with other Addigy® LPU products, and can be used in 1- or 2-component based formulations in combination with isocyanate reactive compounds.
By using it as a primary component in 3D printing formulations, the mechanical properties of the final printed parts can tuned in a wide range to meet the required specifications.
This versatile resin is compatible with a variety of reactive thinners, mixable with other Addigy® LPU products, and can be used in 1- or 2-component based formulations in combination with isocyanate reactive compounds.
储存条件
- Storage in original sealed Covestro container.
- Recommended storage temperature: 10 - 30 °C.
- Keep container dry and tightly closed in a cool and well ventilated place.
- Protect against heat and direct sunlight.
- Recommended storage temperature: 10 - 30 °C.
- Keep container dry and tightly closed in a cool and well ventilated place.
- Protect against heat and direct sunlight.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性特征
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 118 |
| Tensile strength at break xy-direction | ISO 527-2(200 mm/min) | MPa | 24 |
| Glass transition temperature | DIN EN ISO 6721-1 | °C | 70 |
| Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 100 |
命名属性规范
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Color | DIN EN 1557 | Hazen | 7 - 17 |
| Density at 23 °C | DIN EN ISO 2811-3 | g/cm^3 | 1.05 |
| Viscosity at 23 °C | DIN EN ISO 3219 | mPa s | 10,000 - 16,000 |
| Double bond density | % | 6.2 | |
| Appearance | clear | ||
| NCO (blocked) | % | 3.7 |