Addigy® GPU 64D 000000 UV
Additive manufacturing Thermoplastic Polyurethane grade for filament extrusion. Ester type; transparent filament; hydrolysis-stabilised; with special UV stabilizers; good wear resistance
i
市场转换
选择会影响你得到的结果。
关于
材料类型
- TPU
材料
- 弹性体
- 紫外线稳定, 水解稳定
- 3D打印
- 良好的底板粘接力, 良好层间结合力, 低翘曲, 易于打印
- 热塑性聚氨酯
- 透明, 抗磨损
一般特征
无可用数据
储存条件
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性规范
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Appearance | natural color | ||
| Tensile strength z-direction | ISO 527-2 (200 mm/min) | MPa | 18 |
| Impact strength Izod, notched (1A)xz-direction | DIN EN ISO 180 | kJ/m^2 | non-break |
| Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 43 |
| Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 157 |
| Young’s Modulus z-direction | ISO 527-2(1 mm/min) | MPa | 153 |
| Elongation at break z-direction | ISO 527-2(200 mm/min) | % | 160 |
| Glass transition temperature | ISO 6721-1 | °C | - 4 |
| Density | ISO 1183-1 | kg/m^3 | 1229 |
| Shore hardness D | DIN ISO 7619-1 (1s) | 60 - 64 | |
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 400 |
| Impact strength Izod, notched (1A)xy-direction | DIN EN ISO 180 | kJ/m^2 | non-break |