Addigy® GPC 3052RC 000000
Additive manufacturing Polycarbonate grade for filament extrusion. Recycled grade made from pre-consumer material. High viscous, high strength, transparent.
i
市场转换
选择会影响你得到的结果。
关于
材料类型
无可用数据
材料
无可用数据
一般特征
无可用数据
储存条件
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性规范
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Density | ISO 1183-1 | kg/m^3 | 1220 |
| Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 2070 |
| Glass transition temperature | DIN EN ISO 11357-1 | °C | 150 - 153 |
| Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 60 |
| Appearance | natural color | ||
| Impact strength xz-direction | ISO 180/1U | kJ/m^2 | 178 |
| Impact strength xy-direction | ISO 180/1U | kJ/m^2 | 185 |
| Young’s Modulus z-direction | ISO 527-2(1 mm/min) | MPa | 1940 |
| Vicat softening temperature 50 N; 50 °C/h | ISO 306 | °C | 149 |
| Melt volume rate 300 °C; 1.2 kg | ISO 1133 | cm^3 / 10 min | 6.5 - 7.5 |
| Elongation at break z-direction | % | 5 | |
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 27 |
| Tensile strength z-direction | ISO 527-2(200 mm/min) | MPa | 53 |
下载
-
技术数据表
-
安全数据表无可用直接下载，请访问 www.productsafetyfirst.covestro.com