Addigy® FPU 77D 000 A X1010
Additive manufacturing Thermoplastic Polyuethane grade for fused filament fabrication. Aromatic ether-based type; tough and rigid; transparent filament.
i
市场转换
选择会影响你得到的结果。
关于
材料类型
- TPU
材料
- 3D打印
- 良好表面效果, 良好的底板粘接力, 良好层间结合力, 易于打印
- 泡沫
- 硬质
- 热塑性聚氨酯
- 透明
一般特征
无可用数据
储存条件
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性规范
属性名称 | 测试方法 | 单位 | 数值 |
---|---|---|---|
Young’s Modulus z-direction | ISO 527-2(1 mm/min) | MPa | 370 |
Density | ISO 1183-1 | kg/m^3 | 1190 |
Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 280 |
Tensile strength z-direction | ISO 527-2 (200 mm/min) | MPa | 13 |
Elongation at break z-direction | ISO 527-2 (200 mm/min) | % | 18 |
Appearance | natural color | ||
Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 440 |
Abrasion resistance | ISO 4649 method A | mm^3 | 52 |
Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 27 |
Shore hardness D | DIN ISO 7619-1 (1s) | 77 | |
Vicat softening temperature 10 N, 50 °C/h | ISO 306 | °C | 130 |