Addigy® FPB 2684 000000 A
Additive manufacturing Polycarbonate blend for filament extrusion. Diameter: 1.75 mm Tough and rigid, heat resistant, cold stable, UV stable; easy processing. Natural color.
i
市场转换
选择会影响你得到的结果。
关于
材料类型
无可用数据
材料
无可用数据
一般特征
无可用数据
储存条件
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
样品
无可用数据
包装类型
无可用数据
技术属性和数据表
命名属性规范
| 属性名称 | 测试方法 | 单位 | 数值 |
|---|---|---|---|
| Volume Resistivity | IEC 60093 | Ohm m | 10^14 |
| Vicat softening temperature 50 N; 120 °C/h | ISO 306 | °C | 120 |
| Density | ISO 1183-1 | kg/m^3 | 1130 |
| Impact strength z-direction | ISO 180/1U | kJ/m^2 | 2.12 |
| Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 47 |
| Appearance | natural color | ||
| Heat deflection temperature 1.82 MPa | ASTM D 648 | °C | 110 |
| Young’s Modulus xy-direction | ISO 527-2 (1 mm/min) | MPa | 1930 |
| Tensile strength z-direction | ISO 527-2 (200 mm/min) | MPa | 28 |
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 12 |
| Heat deflection temperature 0.45 MPa | ASTM D 648 | °C | 130 |
| Elongation at break z-direction | ISO 527-2 (200 mm/min) | % | 1.7 |
| Young’s Modulus z-direction | ISO 527-2 (1 mm/min) | MPa | 1990 |
| Melt volume rate 300 °C; 1.2 kg | ISO 1133 | cm^3 / 10 min | 18 |
| Impact strength xy-direction | ISO 180/1U | 104 |