Addigy® GPC 3D1000C 000000

Additive manufacturing Polycarbonate grade for filament extrusion. Transparent, tough and rigid; easy processing, low viscosity

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

3D Print
Good surface finish, Low warping, Easy printable, Good layer adhesion
Plastics
Transparent
Coatings, paints & inks
Low viscous
Foams
Rigid

General Characterization

No data available

Storage Conditions

The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Specifications

Property Name Test Method Unit Value
Appearance natural color
Melt volume rate 300 °C; 1.2 kg ISO 1133 cm^3 / 10 min 34
Elongation at break xy-direction ISO 527-2(1 mm/min) % 4
Impact strength yz-directionCharpy unnotched ISO 179-1 kJ/m^2 64
Tensile strength xy-direction ISO 527-2(200 mm/min) MPa 63
Density ISO 1183-1 kg/m^3 1210
Vicat softening temperature 50 N; 50 °C/h ISO 306 °C 112
Young’s Modulus xy-direction ISO 527-2(1 mm/min) MPa 2010

Downloads

Technical Data Sheet
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com

Do you want to know more about Addigy® GPC 3D1000C 000000?
Get in touch with our experts!

Contact form image Zoe

How would you describe yourself?

Compare