Makrolon® TC8030
high thermal conductivity; LED heat sinks (metal replacement); components for heat dissipation
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Polycarbonate
Material
- Plastics
- Thermal conductive, Heat resistant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 2.0 mm | Class | V-0 |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.38 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.24 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 1.5 mm | °C | 930 |
| Glow wire test (GWIT) | IEC 60695-2-13 | 3.0 mm | °C | 990 |
| Oxygen index | ISO 4589-2 | Method A | % | 74 |
| Relative temperature index (Tensile impact strength) | UL 746B | °C | 130 | |
| Relative temperature index (Tensile strength) | UL 746B | °C | 130 | |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 147 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 141 |
| Thermal conductivity, in-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 14 |
| Thermal conductivity, in-plane | ISO 22007-2 | W/(m*K) | 22 | |
| Thermal conductivity, through-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 1.3 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 148 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | < 5.0 |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C | kJ/m² | < 5.0 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 7100 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 1 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 51 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | < 5.0 |
| Strain at break | ISO 527-1,-2 | 5 mm/min | % | 1 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 37 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 6200 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 330 °C | Pa*s | 169 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | Ohm | 1.8E+01 | |
| Volume resistivity | IEC 60093 | Ohm*m | 1.6E+02 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 300 - 330 | |
| Injection molding - Mold temperature | ISO 294 | °C | 65 - 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1420 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com