Makrolon® TC110 FR
moderate thermal conductivity; MVR (300 °C/1.2 kg) 5.0 cm³/10 min; high viscosity; flame retardant; electrically insulating; components for heat dissipation
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- Thermal conductive
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 4 | |
| Mold Temperatures | - | °C | 80 - 90 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 1.5 mm | Class | V0 |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.54 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.36 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 143 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 132 |
| Thermal conductivity, in-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 0.8 |
| Thermal conductivity, through-plane | ASTM E1461 | 23 °C; 50 % r. h. | W/(m*K) | 0.2 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 145 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | 90 C |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 6000 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 4 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 97 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 95 |
| Nominal strain at break | ISO 527-1,-2 | 5 mm/min | % | 4.3 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 10 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 3200 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 52 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 6000 |
| Yield strain | ISO 527-1,-2 | 5 mm/min | % | 3 |
| Yield stress | ISO 527-1,-2 | 5 mm/min | MPa | 52 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C | Pa*s | 160 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 5 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm | % | 0.3 - 0.4 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 275 |
| Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 39 |
| Surface resistivity | IEC 60093 | Ohm | >=1E+15 | |
| Volume resistivity | IEC 60093 | Ohm*m | >=1E+15 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 280 | |
| Injection molding - Mold temperature | ISO 294 | °C | 90 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1450 |