Makrolon® RW2407 RE
MVR (300 °C/1.2 kg) 19 cm³/10 min; low viscosity; easy release; UV stabilized; variable content of filler for high reflectance application
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Barrel Temperatures - Front | - | °C | 280 - 290 | |
| Barrel Temperatures - Middle | - | °C | 270 - 280 | |
| Barrel Temperatures - Nozzle | - | °C | 290 - 300 | |
| Barrel Temperatures - Rear | - | °C | 250 - 260 | |
| Dry Air Drying Temperature | - | °C | 120 | |
| Dry Air Drying Time | - | h | 2 - 3 | |
| Hold Pressure (% of injection pressure) | - | % | 50 - 75 | |
| Melt temperatures | - | °C | 280 - 320 | |
| Moisture Content max. (%) | - | % | <= 0,02 | |
| Mold Temperatures | - | °C | 80 - 120 | |
| Peripheral Screw Speed | - | m/s | 0.05 - 0.2 | |
| Plastic Back Pressure (specific) | - | bar | 50 - 150 | |
| Shot-to-Cylinder Size | - | % | 30 - 70 | |
| Standard Melt temperature | - | °C | 300 | |
| Vent Depth | - | mm | 0.025 - 0.075 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | Class | V-2 (WT) | |
| Burning behavior UL 94 [UL recognition] | UL 94 | 2.7 mm | Class | HB (WT) |
| Burning behavior UL 94 [UL recognition] | UL 94 | 3.0 mm | Class | HB (WT) |
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.75 mm | Class | V-2 (WT) |
| Glow wire test (GWFI) | IEC 60695-2-12 | 0.75 mm | °C | 850 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
| Relative temperature index (Electric strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
| Relative temperature index (Tensile impact strength) [UL recognition] | UL 746B | 1.5 mm | °C | 115 |
| Relative temperature index (Tensile strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 144 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2500 - 2750 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 6 - 6.5 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 96 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 75 - 80 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C | kJ/m² | 15 (C) |
| Nominal strain at break | ISO 527-1,-2 | 5 mm/min | % | >50 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 43 - 50 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 4800 - 5100 |
| Strain at break | ISO 527-1,-2 | 5 mm/min | % | 80 - 110 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 50 - 60 |
| Yield strain | ISO 527-1,-2 | 5 mm/min | % | 5.5 |
| Yield stress | ISO 527-1,-2 | 5 mm/min | MPa | 60 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Light reflection | JIS 8722 | 4 mm | % | 96 - 97 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 19 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 280 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1240 - 1340 |