Makrolon® LED5101

MVR (300 °C/1.2 kg) 34 cm³/10 min; light guides; PC with highest transmission; low viscosity; easy release

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

No data available

Material

No data available

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Burning behavior UL 94 UL 94 2.9 mm Class HB (CL)
Burning behavior UL 94 UL 94 0.75 mm Class V-2 (CL)
Burning rate (US-FMVSS) ISO 3795 >=1.0 mm mm/min passed
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Coefficient of linear thermal expansion, transverse ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Flash ignition temperature ASTM D1929 °C 480
Glass transition temperature ISO 11357-1,-2 10 °C/min °C 145
Glow wire test (GWFI) IEC 60695-2-12 1.0 mm °C 850 - 850
Glow wire test (GWFI) IEC 60695-2-12 1.5 mm °C 875
Glow wire test (GWFI) IEC 60695-2-12 3.0 mm °C 930
Glow wire test (GWIT) IEC 60695-2-13 0.75 mm °C 875
Glow wire test (GWIT) IEC 60695-2-13 1.5 mm °C 875
Glow wire test (GWIT) IEC 60695-2-13 3.0 mm °C 900
Oxygen index ISO 4589-2 Method A % 28
Relative temperature index (Electric strength) UL 746B 1.5 mm °C 125
Relative temperature index (Tensile impact strength) UL 746B 1.5 mm °C 115
Relative temperature index (Tensile strength) UL 746B 1.5 mm °C 125
Resistance to heat (ball pressure test) IEC 60695-10-2 °C 136
Self ignition temperature ASTM D1929 °C 550
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 138
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 125
Thermal conductivity, cross-flow ISO 8302 23 °C; 50 % r. h. W/(m*K) 0.2
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 146
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 145 - 145
Property Name Standard Test condition Unit Value
Ball indentation hardness ISO 2039-1 N/mm² 115
Charpy impact strength ISO 179-1eU -30 °C kJ/m² N
Charpy impact strength ISO 179-1eU -60 °C kJ/m² N
Charpy impact strength ISO 179-1eU 23 °C kJ/m² N
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA -30 °C; 3 mm kJ/m² 12C
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA 23 °C; 3 mm kJ/m² 60P(C)
Flexural modulus ISO 178 2 mm/min MPa 2350 - 2350
Flexural strain at flexural strength ISO 178 2 mm/min % 7.1 - 7.1
Flexural strength ISO 178 2 mm/min MPa 97
Flexural stress at 3.5 % strain ISO 178 2 mm/min MPa 73 - 73
Izod notched impact strength ISO 7391/b.o. ISO 180-A 23 °C; 3 mm kJ/m² 55P
Izod notched impact strength ISO 7391/b.o. ISO 180-A -30 °C; 3 mm kJ/m² 12C
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Puncture energy ISO 6603-2 -30 °C J 60
Puncture energy ISO 6603-2 23 °C J 55 - 55
Puncture maximum force ISO 6603-2 -30 °C N 5900
Puncture maximum force ISO 6603-2 23 °C N 4900 - 4900
Strain at break b.o. ISO 527-1,-2 50 mm/min % 125
Stress at break ISO 527-1,-2 50 mm/min MPa 60
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2350 - 2350
Yield strain ISO 527-1,-2 50 mm/min % 6
Yield stress ISO 527-1,-2 50 mm/min MPa 63
Property Name Standard Test condition Unit Value
Haze for transparent materials ISO 14782 3 mm % < 0.5
Luminous transmittance (clear transparent materials) ISO 13468-2 1 mm % 90
Luminous transmittance (clear transparent materials) ISO 13468-2 2 mm % 90
Luminous transmittance (clear transparent materials) ISO 13468-2 4 mm % > 89
Luminous transmittance (clear transparent materials) ISO 13468-2 3 mm % > 89
Refractive index ISO 489 Procedure A 1.584
Property Name Standard Test condition Unit Value
Melt volume-flow rate ISO 1133 300 °C; 1.2 kg cm³/10 min 34
Molding shrinkage, normal ISO 294-4 60x60x2 mm; 500 bar % 0.7
Molding shrinkage, parallel ISO 294-4 60x60x2 mm; 500 bar % 0.65
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 250
Comparative tracking index CTI M IEC 60112 Solution B Rating 125M
Dissipation factor IEC 60250 1 MHz 10^-4^ 95
Dissipation factor IEC 60250 100 Hz 10^-4^ 5
Electrical strength IEC 60243-1 1 mm kV/mm 34
Relative permittivity IEC 60250 1 MHz 3.0
Relative permittivity IEC 60250 100 Hz 3.1
Surface resistivity IEC 60093 Ohm 1E16
Volume resistivity IEC 60093 Ohm*m 1E14
Property Name Standard Test condition Unit Value
Injection molding-Injection velocity ISO 294 mm/s 200
Injection molding-Melt temperature ISO 294 °C 280 - 280
Injection molding-Mold temperature ISO 294 °C 80 - 80
Property Name Standard Test condition Unit Value
Bulk density ISO 60 Pellets kg/m³ 660
Density ISO 1183-1 kg/m³ 1190 - 1190
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.12
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.3

Downloads

Technical Data Sheet
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Related topics

Do you want to know more about Makrolon® LED5101?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare