Makrolon® FU1007

MVR (300 °C/1.2 kg) 9.0 cm³/10 min; special grade for furniture applications with demands regarding fire standards UNI 8456, 8457, 9174 and 9175; medium viscosity; UV stabilized; easy release

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

Plastics
UV stable

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Application of flame from small burner DIN 53438-1,-3 Method K and F; 2.0 mm Class K1, F1
Burning behavior UNI 9177 (incl.9174; 8456; 8457) UNI 9177 4.0 mm Class 1
Burning behavior UNI 9177 (incl.9174; 8456; 8457) UNI 9177 6.0 mm Class 1
Burning rate (US-FMVSS) ISO 3795 >=1.0 mm mm/min passed
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Coefficient of linear thermal expansion, transverse ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.65
Flash ignition temperature ASTM D1929 °C 480
Glass transition temperature ISO 11357-1,-2 10 °C/min °C 143
Oxygen index ISO 4589-2 Method A % 28
Relative temperature index (Electric strength) UL 746B 1.5 mm °C 125
Relative temperature index (Tensile impact strength) UL 746B 1.5 mm °C 115
Relative temperature index (Tensile strength) UL 746B 1.5 mm °C 125
Resistance to heat (ball pressure test) IEC 60695-10-2 °C 135
Self ignition temperature ASTM D1929 °C 550
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 136
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 124
Thermal conductivity, cross-flow ISO 8302 23 °C; 50 % r. h. W/(m*K) 0.2
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 145
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 144 - 144
Property Name Standard Test condition Unit Value
Ball indentation hardness ISO 2039-1 N/mm² 116
Charpy impact strength ISO 179-1eU -30 °C kJ/m² N
Charpy impact strength ISO 179-1eU 23 °C kJ/m² N
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA -30 °C; 3 mm kJ/m² 14C
Charpy notched impact strength ISO 7391/b.o. ISO 179-1eA 23 °C; 3 mm kJ/m² 75P
Flexural modulus ISO 178 2 mm/min MPa 2400 - 2400
Flexural strain at flexural strength ISO 178 2 mm/min % 7 - 7
Flexural strength ISO 178 2 mm/min MPa 98
Flexural stress at 3.5 % strain ISO 178 2 mm/min MPa 74 - 74
Izod notched impact strength ISO 7391/b.o. ISO 180-A 23 °C; 3 mm kJ/m² 70P
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Puncture energy ISO 6603-2 -30 °C J 65
Puncture energy ISO 6603-2 23 °C J 60 - 60
Puncture maximum force ISO 6603-2 -30 °C N 6300
Puncture maximum force ISO 6603-2 23 °C N 5400 - 5400
Strain at break b.o. ISO 527-1,-2 50 mm/min % 120
Stress at break ISO 527-1,-2 50 mm/min MPa 70
Tensile creep modulus ISO 899-1 1 h MPa 2200
Tensile creep modulus ISO 899-1 1000 h MPa 1900
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2400 - 2400
Yield strain ISO 527-1,-2 50 mm/min % 6.1
Yield stress ISO 527-1,-2 50 mm/min MPa 67
Property Name Standard Test condition Unit Value
Haze for transparent materials ISO 14782 3 mm % < 0.8
Luminous transmittance (clear transparent materials) ISO 13468-2 1 mm % 89
Luminous transmittance (clear transparent materials) ISO 13468-2 2 mm % 89
Luminous transmittance (clear transparent materials) ISO 13468-2 4 mm % 87
Luminous transmittance (clear transparent materials) ISO 13468-2 3 mm % 88
Refractive index ISO 489 Procedure A 1.586
Property Name Standard Test condition Unit Value
Melt mass-flow rate ISO 1133 300 °C; 1.2 kg g/10 min 10
Melt volume-flow rate ISO 1133 300 °C; 1.2 kg cm³/10 min 9
Molding shrinkage, normal ISO 294-4 60x60x2 mm; 500 bar % 0.7
Molding shrinkage, parallel ISO 294-4 60x60x2 mm; 500 bar % 0.65
Molding shrinkage, parallel/normal b.o. ISO 2577 Value range based on general practical experience % 0.6 - 0.8
Property Name Standard Test condition Unit Value
Injection molding-Injection velocity ISO 294 mm/s 200
Injection molding-Melt temperature ISO 294 °C 300 - 300
Injection molding-Mold temperature ISO 294 °C 80 - 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1200 - 1200
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.12
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.3

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Makrolon® FU1007?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare