Makrolon® FR7087

MVR (300 °C/1.2 kg) 12 cm³/10 min; flame retardant; UL 94V-0/2.2 mm and 5VA/3.0 mm; medium viscosity; UV stabilized; easy release; electrical/electronic

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

Plastics
UV stable, Optical quality, Clear

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 285 - 305
Barrel Temperatures - Middle - °C 270 - 290
Barrel Temperatures - Nozzle - °C 270 - 305
Barrel Temperatures - Rear - °C 250 - 270
Dry Air Drying Temperature - °C 120 - 120
Dry Air Drying Time - h 4 - 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt Temperatures - °C 280 - 320
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 70 - 110
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 100 - 200
Shot-to-Cylinder Size - % 30 - 70
Standard Melt Temperature - °C 300
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 UL 94 2.2 mm Class V-0
Burning behavior UL 94 (1.5 mm) UL 94 1.5 mm Class V-2
Burning behavior UL 94-5V UL 94 3.0 mm Class 5VA
Glow wire test (GWFI) IEC 60695-2-12 1.5 mm °C 960
Glow wire test (GWFI) IEC 60695-2-12 3.0 mm °C 960
Glow wire test (GWFI) IEC 60695-2-12 2.2 mm °C 960
Glow wire test (GWIT) IEC 60695-2-13 1.5 mm °C 930
Glow wire test (GWIT) IEC 60695-2-13 2.2 mm °C 930
Glow wire test (GWIT) IEC 60695-2-13 3.0 mm °C 960
Relative temperature index (Electric strength) UL 746B 1.5 mm °C 125
Relative temperature index (Tensile impact strength) UL 746B 1.5 mm °C 80
Relative temperature index (Tensile strength) UL 746B 1.5 mm °C 85
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 118
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 106
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 124
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 123 - 123
Property Name Standard Test condition Unit Value
Charpy impact strength ISO 179-1eU 23 °C kJ/m² N
Izod notched impact strength ISO 7391/b.o. ISO 180-A 23 °C; 3 mm kJ/m² 8C
Izod notched impact strength ISO 7391/b.o. ISO 180-A -30 °C; 3 mm kJ/m² 8C
Strain at break b.o. ISO 527-1,-2 50 mm/min % 100
Stress at break ISO 527-1,-2 50 mm/min MPa 75
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2500 - 2500
Yield strain ISO 527-1,-2 50 mm/min % 5
Yield stress ISO 527-1,-2 50 mm/min MPa 75
Property Name Standard Test condition Unit Value
Haze for transparent materials ISO 14782 3 mm % 0.9
Luminous transmittance ISO 13468-2 3 mm % 88
Property Name Standard Test condition Unit Value
Melt mass-flow rate ISO 1133 300 °C; 1.2 kg g/10 min 12
Melt volume-flow rate ISO 1133 300 °C; 1.2 kg cm³/10 min 12
Property Name Standard Test condition Unit Value
Injection molding-Injection velocity ISO 294 mm/s 200
Injection molding-Melt temperature ISO 294 °C 290 - 290
Injection molding-Mold temperature ISO 294 °C 80 - 80

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Makrolon® FR7087?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare