Makrolon® FR6020 RE
polycarbonate; medium viscosity; easy release; UV stabilized; flame retardant; chlorine- and bromine-free flame retardancy; non-reinforced; good hydrolysis resistance; impact modified; Information technology; electrical/electronic
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- CQ renewable attributed
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 | UL 94 | 2.0 mm | Class | V-0 |
| Burning behavior UL 94 (1.5 mm) | UL 94 | Class | V-0 | |
| Burning behavior UL 94-5V | UL 94 | 2.0 mm | Class | 5VB |
| Burning behavior UL 94-5V | UL 94 | 3.0 mm | Class | 5VA |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.58 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.49 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 127 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 114 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 136 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 134 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C | kJ/m² | 69 |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -30 °C | kJ/m² | 33 |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2430 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 90 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C | kJ/m² | 67 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C | kJ/m² | 26 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | > 100 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 58 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2380 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 58 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 9 |
| Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience | % | 0.6 - 0.8 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Melt temperature | ISO 294 | °C | 280 - 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1200 |