Makrolon® FR6005 HF

MVR (300 °C/1.2 kg) 16 cm³/10 min; low viscosity; easy release; flame retardant; impact modified; electrical/electronic; housing parts

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

No data available

Material

No data available

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 280 - 290
Barrel Temperatures - Middle - °C 270 - 280
Barrel Temperatures - Nozzle - °C 290 - 300
Barrel Temperatures - Rear - °C 250 - 260
Dry Air Drying Temperature - °C 120
Dry Air Drying Time - h 2 - 3
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 280 - 320
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 80 - 120
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 300
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 UL 94 3.0 mm Class V-0
Burning behavior UL 94 UL 94 1.5 mm Class V-0
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.66
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.61
Glow wire test (GWFI) IEC 60695-2-12 1.5 mm °C 960
Glow wire test (GWFI) IEC 60695-2-12 3.0 mm °C 960
Glow wire test (GWIT) IEC 60695-2-13 1.5 mm °C 850
Glow wire test (GWIT) IEC 60695-2-13 3.0 mm °C 900
Resistance to heat (ball pressure test) IEC 60695-10-2 °C 134
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 133
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 118
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 141
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 138
Property Name Standard Test condition Unit Value
Charpy notched impact strength ISO 7391/b.o. ISO 179/1eA 23 °C kJ/m² 56P
Charpy notched impact strength ISO 7391/b.o. ISO 179/1eA -30 °C kJ/m² 18C
Flexural modulus ISO 178 2 mm/min MPa 2320
Flexural strength ISO 178 2 mm/min MPa 92
Izod notched impact strength ISO 7391/b.o. ISO 180/A 23 °C/ 3 mm kJ/m² 56P
Izod notched impact strength ISO 7391/b.o. ISO 180/A -30 °C/ 3 mm kJ/m² 16C
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Puncture energy ISO 6603-2 23 °C J 51
Puncture impact properties - maximum force ISO 6603-2 23 °C N 5000
Strain at break b.o. ISO 527-1,-2 50 mm/min % 100
Stress at break ISO 527-1,-2 50 mm/min MPa 55
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2310
Yield strain ISO 527-1,-2 50 mm/min % 5.7
Yield stress ISO 527-1,-2 50 mm/min MPa 60
Property Name Standard Test condition Unit Value
Melt volume-flow rate ISO 1133 300 °C/ 1.2 kg cm³/10 min 16
Molding shrinkage, parallel/normal b.o. ISO 2577 Value range based on general practical experience % 0.6 - 0.8
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 200
Injection molding - Melt temperature ISO 294 °C 300
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1200

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com