Makrolon® CF9920 R30 RE
PC blend filled with carbon fiber; polycarbonate; flame retardant; With 30% Post Consumer Recycled PC
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
- Plastics
- CQ renewable attributed, CQ mechanical recycled
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Dry Air Drying Temperature | - | °C | 80 | |
| Dry Air Drying Time | - | h | 4 | |
| Melt temperatures | - | °C | 270 - 310 | |
| Mold Temperatures | - | °C | 60 - 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.75 mm | Class | V-0 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 92 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 102 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 16500 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 230 |
| Izod impact strength | ISO 180/U | 23 °C | kJ/m² | 27 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C | kJ/m² | 7 |
| Strain at break | ISO 527-1,-2 | 5 mm/min | % | 1.4 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 162 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 19000 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt mass-flow rate | ISO 1133 | 260 °C/ 5 kg | g/10 min | 16 |
| Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 14 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1310 |