- Plastics
Makrolon® 8345
MVR (300 °C/1.2 kg) 3.0 cm³/10 min; 35 % glass fiber reinforced; high viscosity; easy release
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Polycarbonate
Material
- Plastics
- Dimensionally stable
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Application of flame from small burner | DIN 53438-1,-3 | Method K and F/ 2.0 mm | Class | K1, F1 |
| Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | 1.5 mm | Class | V-1 |
| Burning behavior UL 94 [UL recognition] | UL 94 | 3.0 mm | Class | V-0 |
| Burning rate (US-FMVSS) | ISO 3795 | >=1.0 mm | mm/min | passed |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.6 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.2 |
| Flash ignition temperature | ASTM D1929 | °C | 470 | |
| Glow wire test (GWFI) | IEC 60695-2-12 | 1.5 mm | °C | 960 |
| Glow wire test (GWFI) | IEC 60695-2-12 | 3.0 mm | °C | 960 |
| Needle flame test | IEC 60695-11-5 | Method F/ 1.5 mm | s | 120 |
| Needle flame test | IEC 60695-11-5 | Method F/ 2.0 mm | s | 120 |
| Needle flame test | IEC 60695-11-5 | Method F/ 3.0 mm | s | 120 |
| Needle flame test | IEC 60695-11-5 | Method K/ 3.0 mm | s | 120 |
| Needle flame test | IEC 60695-11-5 | Method K/ 1.5 mm | s | 60 |
| Needle flame test | IEC 60695-11-5 | Method K/ 2.0 mm | s | 60 |
| Oxygen index | ISO 4589-2 | Method A | % | 35 |
| Relative temperature index (Electric strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
| Relative temperature index (Tensile impact strength) [UL recognition] | UL 746B | 1.5 mm | °C | 115 |
| Relative temperature index (Tensile strength) [UL recognition] | UL 746B | 1.5 mm | °C | 125 |
| Resistance to heat (ball pressure test) | IEC 60695-10-2 | °C | 136 | |
| Self ignition temperature | ASTM D1929 | °C | 550 | |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 144 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 140 |
| Thermal conductivity, through-plane | ISO 8302 | 23 °C; 50 % r. h. | W/(m*K) | 0.24 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 149 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 148 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Ball indentation hardness | ISO 2039-1 | N/mm² | 175 | |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | 40C |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C/ 3 mm | kJ/m² | 8C |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 8600 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 2.5 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 170 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 8C |
| Puncture energy | ISO 6603-2 | -30 °C | J | 5 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 5 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 900 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 900 |
| Strain at break | ISO 527-1,-2 | 5 mm/min | % | 1.8 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 110 |
| Tensile creep modulus | ISO 899-1 | 1 h | MPa | 9000 |
| Tensile creep modulus | ISO 899-1 | 1000 h | MPa | 8500 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 9400 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 1.9 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 113 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt mass-flow rate | ISO 1133 | 300 °C/ 1.2 kg | g/10 min | 3.5 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 3 |
| Molding shrinkage, parallel/normal | b.o. ISO 2577 | Value range based on general practical experience | % | 0.3 - 0.5 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 175 |
| Comparative tracking index CTI M | IEC 60112 | Solution B | Rating | 125M |
| Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 90 |
| Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 10 |
| Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 36 |
| Electrolytic corrosion | IEC 60426 | Rating | A1 | |
| Relative permittivity | IEC 60250 | 1 MHz | 3.6 | |
| Relative permittivity | IEC 60250 | 100 Hz | 3.6 | |
| Surface resistivity | IEC 60093 | Ohm | 1E16 | |
| Volume resistivity | IEC 60093 | Ohm*m | 1E14 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 300 | |
| Injection molding - Mold temperature | ISO 294 | °C | 110 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Bulk density | ISO 60 | Pellets | kg/m³ | 670 |
| Density | ISO 1183-1 | kg/m³ | 1480 | |
| Glass fiber content | b.o. ISO 3451-1 | Method A | % | 35 |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.1 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.2 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com
-
Viscosity Shear Rate Makrolon® 8345 (Multipoint Data Sheet) Viskosität Schergeschwindigkeit Makrolon® 8345 (Multipoint Data Sheet)
-
Dynamic Shear Modulus – Temperature Makrolon® 8345 (Multipoint Data Sheet) Dynamischer Schubmodul - Temperatur Makrolon® 8345 (Multipoint Data Sheet)
-
Stress-Strain Makrolon® 8345 (Multipoint Data Sheet) Spannung-Dehnung Makrolon® 8345 (Multipoint Data Sheet)
-
Secant modulus - Strain Makrolon® 8345 (Multipoint Data Sheet) Sekantenmodul-Dehnung Makrolon® 8345 (Multipoint Data Sheet)