Makrolon® 3638
MVR (300 °C/1.2 kg) 2.0 cm³/10 min; high viscosity; food contact quality; biocompatible according to many ISO 10993-1 test requirements; pharmaceutical applications; medical devices
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.7 |
| Flash ignition temperature | ASTM D1929 | °C | 480 | |
| Glass transition temperature | ISO 11357-1,-2 | 10 °C/min | °C | 152 |
| Oxygen index | ISO 4589-2 | Method A | % | 26 |
| Resistance to heat (ball pressure test) | IEC 60695-10-2 | °C | 144 | |
| Self ignition temperature | ASTM D1929 | °C | 550 | |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 145 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 132 |
| Thermal conductivity, through-plane | ISO 8302 | 23 °C; 50 % r. h. | W/(m*K) | 0.2 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 151 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 150 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Ball indentation hardness | ISO 2039-1 | N/mm² | 108 | |
| Charpy impact strength | ISO 179/1eU | -30 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | -60 °C | kJ/m² | N |
| Charpy impact strength | ISO 179/1eU | 23 °C | kJ/m² | N |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | -30 °C/ 3 mm | kJ/m² | 20C(P) |
| Charpy notched impact strength | ISO 21305/based on ISO 179/1eA | 23 °C/ 3 mm | kJ/m² | 75P |
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2300 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 7.2 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 94 |
| Flexural stress at 3.5 % strain | ISO 178 | 2 mm/min | MPa | 70 |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | 23 °C/ 3 mm | kJ/m² | 65P |
| Izod notched impact strength | ISO 21305/based on ISO 180/A | -30 °C/ 3 mm | kJ/m² | 55P(C) |
| Nominal strain at break | ISO 527-1,-2 | 50 mm/min | % | > 50 |
| Puncture energy | ISO 6603-2 | -30 °C | J | 60 |
| Puncture energy | ISO 6603-2 | 23 °C | J | 55 |
| Puncture impact properties - maximum force | ISO 6603-2 | -30 °C | N | 6400 |
| Puncture impact properties - maximum force | ISO 6603-2 | 23 °C | N | 5500 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | 100 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 65 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2300 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 6.6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 64 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt mass-flow rate | ISO 1133 | 300 °C/ 1.2 kg | g/10 min | 2.5 |
| Melt volume-flow rate | ISO 1133 | 300 °C/ 1.2 kg | cm³/10 min | 2 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm³/ 500 bar | % | 0.8 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm³/ 500 bar | % | 0.75 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 200 | |
| Injection molding - Melt temperature | ISO 294 | °C | 310 | |
| Injection molding - Mold temperature | ISO 294 | °C | 90 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Bulk density | ISO 60 | Pellets | kg/m³ | 660 |
| Density | ISO 1183-1 | kg/m³ | 1200 | |
| Gas permeation | b.o. ISO 2556 | Nitrogen/ 100 µm film | cm³/(m²*24 h*bar) | 140 |
| Gas permeation | b.o. ISO 2556 | Carbon dioxide/ 100 µm film | cm³/(m²*24 h*bar) | 4200 |
| Gas permeation | b.o. ISO 2556 | Oxygen/ 100 µm film | cm³/(m²*24 h*bar) | 740 |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.12 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.3 |
| Water vapor permeability | ISO 15106-1 | 23 °C; 85 % RH/ 100 µm film | g/(m²*24 h) | 15 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com