Makrolon® 1899

MVR (300 °C/1.2 kg) 16 cm³/10 min; special flame retardent system; UL 94V-0/0.75 mm; impact modified; medium viscosity; easy release; Vicat softening temperature 50 N, 50 °C/h = 110 °C; battery housing

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • Polycarbonate

Material

Plastics
Impact resistant, Flame retardant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 250 - 265
Barrel Temperatures - Middle - °C 240 - 250
Barrel Temperatures - Nozzle - °C 245 - 265
Barrel Temperatures - Rear - °C 230 - 240
Dry Air Drying Temperature - °C 90
Dry Air Drying Time - h 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 240 - 280
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 70 - 110
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 100 - 200
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 260
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 [UL recognition] UL 94 0.75 mm Class V-0
Burning behavior UL 94-5V UL 94 3.0 mm Class 5VA (Covestro Test)
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.7
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.7
Flash ignition temperature ASTM D1929 °C 460
Glow wire test (GWFI) IEC 60695-2-12 1.0 mm °C 960
Oxygen index ISO 4589-2 Method A % 35
Relative temperature index (Electric strength) [UL recognition] UL 746B 0.75 mm °C 80
Relative temperature index (Tensile impact strength) [UL recognition] UL 746B 0.75 mm °C 80
Relative temperature index (Tensile strength) [UL recognition] UL 746B 0.75 mm °C 80
Self ignition temperature ASTM D1929 °C 500
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 105
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 96
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 110
Property Name Standard Test condition Unit Value
Charpy impact strength ISO 179/1eU 23 °C kJ/m² N
Flexural modulus ISO 178 2 mm/min MPa 2600
Flexural strain at flexural strength ISO 178 2 mm/min % 5.8
Flexural strength ISO 178 2 mm/min MPa 100
Flexural stress at 3.5 % strain ISO 178 2 mm/min MPa 82
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Puncture energy ISO 6603-2 -30 °C J 55
Puncture energy ISO 6603-2 23 °C J 50
Puncture impact properties - maximum force ISO 6603-2 -30 °C N 5400
Puncture impact properties - maximum force ISO 6603-2 23 °C N 4500
Strain at break b.o. ISO 527-1,-2 50 mm/min % 115
Stress at break ISO 527-1,-2 50 mm/min MPa 60
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2600
Yield strain ISO 527-1,-2 50 mm/min % 4.8
Yield stress ISO 527-1,-2 50 mm/min MPa 68
Property Name Standard Test condition Unit Value
Melt mass-flow rate ISO 1133 300 °C/ 1.2 kg g/10 min 16.5
Melt volume-flow rate ISO 1133 300 °C/ 1.2 kg cm³/10 min 16
Molding shrinkage, normal ISO 294-4 60x60x2 mm/ 500 bar % 0.65
Molding shrinkage, parallel ISO 294-4 60x60x2 mm/ 500 bar % 0.6
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 250
Comparative tracking index CTI M IEC 60112 Solution B Rating 100M
Property Name Standard Test condition Unit Value
Injection molding - Injection velocity ISO 294 mm/s 200
Injection molding - Melt temperature ISO 294 °C 260
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Bulk density ISO 60 Pellets kg/m³ 640
Density ISO 1183-1 kg/m³ 1200
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.12
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.3

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Secant modulus - Strain Makrolon® 1899 (Multipoint Data Sheet) Sekantenmodul-Dehnung Makrolon® 1899 (Multipoint Data Sheet)
Stress-Strain Makrolon® 1899 (Multipoint Data Sheet) Spannung-Dehnung Makrolon® 1899 (Multipoint Data Sheet)
Viscosity Shear Rate Makrolon® 1899 (Multipoint Data Sheet) Viskosität Schergeschwindigkeit Makrolon® 1899 (Multipoint Data Sheet)

Do you want to know more about Makrolon® 1899?
Get in touch with our experts!

Contact form image Zoe

How would you describe yourself?

What type of material are you interested in?

What type of inquiry is this?

How can we contact you?

* Mandatory Fields

Compare