Submit
  • Plastics

Bayblend® T88 GF-10 HI

Rubber modified (PC+SAN) blend; 10% glass fibre reinforced; Vicat/B 120 temperature = 130 °C; very good flow; improved impact strength; improved elongation at break; for demanding applications in the automotive interior

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • PC+ABS blend

Material

Plastics
Heat resistant, Impact resistant, Dimensionally stable

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 240 - 270
Barrel Temperatures - Middle - °C 235 - 245
Barrel Temperatures - Nozzle - °C 265 - 275
Barrel Temperatures - Rear - °C 230 - 240
Dry Air Drying Temperature - °C 95 - 110
Dry Air Drying Time - h 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 260 - 280
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 70 - 100
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 270
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 [UL recognition] UL 94 0.85 mm Class HB
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.75
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.43
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 130
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 114
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 130
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 128
Property Name Standard Test condition Unit Value
Izod impact strength ISO 180/U -30 °C kJ/m² 45
Izod impact strength ISO 180/U 23 °C kJ/m² 60
Izod notched impact strength ISO 180/A 23 °C kJ/m² 14
Izod notched impact strength ISO 180/A -30 °C kJ/m² 6
Strain at break ISO 527-1,-2 5 mm/min % 10
Stress at break ISO 527-1,-2 5 mm/min MPa 42
Tensile modulus ISO 527-1,-2 1 mm/min MPa 4300
Yield strain ISO 527-1,-2 5 mm/min % 4.2
Yield stress ISO 527-1,-2 5 mm/min MPa 60
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^/ 260 °C Pa*s 215
Melt volume-flow rate ISO 1133 260 °C/ 5 kg cm³/10 min 16
Molding shrinkage, normal ISO 294-4 60x60x2 mm/ 260 °C / MT 80 °C % 0.4 - 0.06
Molding shrinkage, parallel ISO 294-4 60x60x2 mm/ 260 °C / MT 80 °C % 0.4 - 0.6
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 175
Dissipation factor IEC 60250 1 MHz 10^-4^ 127
Dissipation factor IEC 60250 100 Hz 10^-4^ 31
Electrical strength IEC 60243-1 1 mm kV/mm 36
Relative permittivity IEC 60250 1 MHz 3.2
Relative permittivity IEC 60250 100 Hz 3.3
Surface resistivity IEC 60093 Ohm 1E16
Volume resistivity IEC 60093 Ohm*m 1E14
Property Name Standard Test condition Unit Value
Injection molding - Melt temperature ISO 294 °C 260
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1220
Glass fiber content b.o. ISO 3451-1 Method A % 10
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.2
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.5

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Bayblend® T88 GF-10 HI?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

Compare