Bayblend® T85 XAT

(PC+ABS)-Blend; permanent antistatic (VW PV3977); excellent UV-stability; low temperature impact resistance; for Automotive interior applications (e.g. overhead consoles, etc.)

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

No data available

Material

No data available

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 240 - 270
Barrel Temperatures - Middle - °C 235 - 245
Barrel Temperatures - Nozzle - °C 265 - 275
Barrel Temperatures - Rear - °C 230 - 240
Dry Air Drying Temperature - °C 95 - 110
Dry Air Drying Time - h 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt temperatures - °C 260 - 280
Moisture Content max. (%) - % <=0.02
Mold Temperatures - °C 70 - 90
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt temperature - °C 270
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Coefficient of linear thermal expansion, normal ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.8
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.75
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 124
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 104
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 129
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 127
Property Name Standard Test condition Unit Value
Ball indentation hardness ISO 2039-1 New N/mm² 113
Charpy impact strength ISO 179/1eU -30 °C kJ/m² N
Charpy impact strength ISO 179/1eU 23 °C kJ/m² N
Charpy notched impact strength ISO 179/1eA -30 °C kJ/m² 35
Charpy notched impact strength ISO 179/1eA 23 °C kJ/m² 70
Flexural modulus ISO 178 2 mm/min MPa 2270
Flexural strength ISO 178 2 mm/min MPa 87
Izod impact strength ISO 180/U -30 °C kJ/m² N
Izod impact strength ISO 180/U 23 °C kJ/m² N
Izod notched impact strength ISO 180/A 23 °C kJ/m² 55
Izod notched impact strength ISO 180/A -30 °C kJ/m² 35
Nominal strain at break ISO 527-1,-2 50 mm/min % > 50
Stress at break ISO 527-1,-2 50 mm/min MPa 59
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2170
Yield strain ISO 527-1,-2 50 mm/min % 5
Yield stress ISO 527-1,-2 50 mm/min MPa 56
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^/ 260 °C Pa*s 241
Melt volume-flow rate ISO 1133 260 °C/ 5 kg cm³/10 min 15
Molding shrinkage, normal ISO 294-4 60x60x2 mm/ 260 °C / MT 80 °C/ 500 bar % 0.82
Total shrinkage, normal ISO 294-4 60x60x2 mm/ 260 °C / MT 80 °C/ 500 bar % 0.82
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 225
Electrical strength IEC 60243-1 1 mm kV/mm 35
Relative permittivity IEC 60250 1 MHz 3.2
Relative permittivity IEC 60250 100 Hz 4.2
Volume resistivity IEC 60093 Ohm*m 1E14
Property Name Standard Test condition Unit Value
Injection molding - Melt temperature ISO 294 °C 260
Injection molding - Mold temperature ISO 294 °C 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1170
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.2
Water absorption (saturation value) ISO 62 Water at 23 °C % 1

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Related topics

Do you want to know more about Bayblend® T85 XAT?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

Compare