Bayblend® FR3005 HF BBS314
(PC+ABS)-Blend; flame retardant; very easy-flowing; Vicat/B 120 temperature = 96 °C; UL recognition 94 V-0 at 1.5 mm; Components for the electrical/electronics sector
i
Market Switch
Selection will influence the results you get.
About
Product Types
- PC+ABS blend
Material
- Plastics
- Flame retardant
General Characterization
No data available
Storage Conditions
No data available
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Burning behavior UL 94 (1.5 mm) [UL recognition] | UL 94 | 1.5 mm | Class | V-0 |
| Burning behavior UL 94-5V [UL recognition] | UL 94 | 1.8 mm | Class | 5VB |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.72 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.71 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 90 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 79 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 96 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Flexural modulus | ISO 178 | 2 mm/min | MPa | 2800 |
| Flexural strain at flexural strength | ISO 178 | 2 mm/min | % | 5 |
| Flexural strength | ISO 178 | 2 mm/min | MPa | 94 |
| Izod impact strength | ISO 180/U | 23 °C | kJ/m² | N |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 12 |
| Strain at break | b.o. ISO 527-1,-2 | 50 mm/min | % | > 40 |
| Stress at break | ISO 527-1,-2 | 50 mm/min | MPa | 45 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 2700 |
| Yield strain | ISO 527-1,-2 | 50 mm/min | % | 3.6 |
| Yield stress | ISO 527-1,-2 | 50 mm/min | MPa | 60 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 240 °C | Pa*s | 120 |
| Melt volume-flow rate | ISO 1133 | 240 °C/ 5 kg | cm³/10 min | 38 |
| Molding shrinkage, normal | b.o. ISO 2577 | 150x105x3 mm/ 240 °C / MT 80 °C | % | 0.5 - 0.7 |
| Molding shrinkage, parallel | b.o. ISO 2577 | 150x105x3 mm/ 240 °C / MT 80 °C | % | 0.5 - 0.7 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 250 |
| Surface resistivity | IEC 60093 | Ohm | 1E16 | |
| Volume resistivity | IEC 60093 | Ohm*m | 1E15 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Injection molding - Injection velocity | ISO 294 | mm/s | 240 | |
| Injection molding - Melt temperature | ISO 294 | °C | 240 | |
| Injection molding - Mold temperature | ISO 294 | °C | 80 |
| Property Name | Standard | Test condition | Unit | Value |
|---|---|---|---|---|
| Density | ISO 1183-1 | kg/m³ | 1190 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com