Bayblend® FR1514 BBS073

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 136 °C; improved chemical resistance and stress cracking behavior compared to KU2-1514; ball indentation temperature >= 125 °C; UL recognition 94 V-0 at 1.5 mm; suitable as supporting material for energized parts

Contact an Expert
i
Market Switch
Selection will influence the results you get.
Copied to clipboard

About

Product Types

  • PC+ABS blend

Material

Plastics
Chemical resistant, Heat resistant

General Characterization

No data available

Storage Conditions

No data available

Sampling

No data available

Packaging Type

No data available

Technical Properties & Datasheets

Property Name Standard Test condition Unit Value
Barrel Temperatures - Front - °C 230 - 240
Barrel Temperatures - Middle - °C 225 - 235
Barrel Temperatures - Nozzle - °C 255 - 265
Barrel Temperatures - Rear - °C 220 - 230
Dry Air Drying Temperature - °C 80 - 80
Dry Air Drying Time - h 4 - 4
Hold Pressure (% of injection pressure) - % 50 - 75
Melt Temperatures - °C 240 - 280
Moisture Content max. (%) - % <= 0,02
Mold Temperatures - °C 60 - 90
Peripheral Screw Speed - m/s 0.05 - 0.2
Plastic Back Pressure (specific) - bar 50 - 150
Shot-to-Cylinder Size - % 30 - 70
Standard Melt Temperature - °C 260
Vent Depth - mm 0.025 - 0.075
Property Name Standard Test condition Unit Value
Burning behavior UL 94 (1.5 mm) UL 94 1.5 mm Class V-0
Burning behavior UL 94-5V UL 94 2.0 mm Class 5VB
Burning behavior UL 94-5V UL 94 3.0 mm Class 5VA
Coefficient of linear thermal expansion, parallel ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.72
Coefficient of linear thermal expansion, transverse ISO 11359-1,-2 23 to 55 °C 10^-4^/K 0.72
Oxygen index ISO 4589-2 Method A % 30
Temperature of deflection under load ISO 75-1,-2 0.45 MPa °C 126
Temperature of deflection under load ISO 75-1,-2 1.80 MPa °C 114
Vicat softening temperature ISO 306 50 N; 120 °C/h °C 136
Vicat softening temperature ISO 306 50 N; 50 °C/h °C 134 - 134
Property Name Standard Test condition Unit Value
Izod impact strength ISO 180-U 23 °C kJ/m² N
Izod notched impact strength ISO 180-A 23 °C kJ/m² 50
Izod notched impact strength ISO 180-A -30 °C kJ/m² 15
Strain at break b.o. ISO 527-1,-2 50 mm/min % >50
Stress at break ISO 527-1,-2 50 mm/min MPa 59
Tensile modulus ISO 527-1,-2 1 mm/min MPa 2400 - 2400
Yield strain ISO 527-1,-2 50 mm/min % 5
Yield stress ISO 527-1,-2 50 mm/min MPa 63
Property Name Standard Test condition Unit Value
Melt viscosity b.o. ISO 11443-A 1000 s^-1^; 260 °C Pa*s 520
Melt volume-flow rate ISO 1133 260 °C; 5 kg cm³/10 min 16
Molding shrinkage, normal b.o. ISO 2577 150x105x3 mm; 260 °C / MT 80 °C % 0.5 - 0.7
Molding shrinkage, parallel b.o. ISO 2577 150x105x3 mm; 260 °C / MT 80 °C % 0.5 - 0.7
Property Name Standard Test condition Unit Value
Comparative tracking index CTI IEC 60112 Solution A Rating 350
Dissipation factor IEC 60250 1 MHz 10^-4^ 85
Dissipation factor IEC 60250 100 Hz 10^-4^ 20
Electrical strength IEC 60243-1 1 mm kV/mm 35
Relative permittivity IEC 60250 1 MHz 3.1
Relative permittivity IEC 60250 100 Hz 3.2
Surface resistivity IEC 60093 Ohm 1E17
Volume resistivity IEC 60093 Ohm*m 1E15
Property Name Standard Test condition Unit Value
Injection molding-Injection velocity ISO 294 mm/s 240
Injection molding-Melt temperature ISO 294 °C 260 - 260
Injection molding-Mold temperature ISO 294 °C 80 - 80
Property Name Standard Test condition Unit Value
Density ISO 1183-1 kg/m³ 1190 - 1190
Water absorption (equilibrium value) ISO 62 23 °C; 50 % r. h. % 0.2
Water absorption (saturation value) ISO 62 Water at 23 °C % 0.5

Downloads

Technical Data Sheet
Download
Safety Data Sheet
No direct download available, please visit www.productsafetyfirst.covestro.com
Download

Do you want to know more about Bayblend® FR1514 BBS073?
Get in touch with our experts!

Contact form image Zoe

How can we contact you?

* Mandatory Fields

1 product to compare