Addigy® GPU 98AN8 000000 UV
Additive manufacturing Thermoplastic Polyurethane grade for filament extrusion. Aromatic ester-based type; elasticity and flexibility, high mechanical strength, UV resistant, wear and tear resistance. Good extrudability, easy printing. Application e.g. in insoles, fabrics, elastic jigs & fixtures, functional prototyping, tubes, and protective parts.
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Strength at 10 % strain xy-direction | DIN 53504 (200 mm/min) | MPa | 5.4 |
| Strength at 300 % strain xy-direction | DIN 53504 (200 mm/min) | MPa | 24 |
| Rebound resilience 100 % infill | ISO 4662 | % | 28 |
| Elongation at break xy-direction | DIN 53504 (200 mm/min) | % | 408 |
| Abrasion resistance xy-direction | ISO 4649 method A | mm^3 | 130 |
| Density | ISO 1183-1 | kg/m^3 | 1200 |
| Tensile strength xy-direction | DIN 53504 (200 mm/min) | MPa | 32 |
| Shore hardness A | DIN ISO 7619-1 (1s) | 95 - 97 | |
| Appearance | natural color | ||
| Elongation at break z-direction | DIN 53504 (200 mm/min) | % | 244 |
| Tensile strength z-direction | DIN 53504 (200 mm/min) | MPa | 13 |
| Tear resistance xy-direction | DIN ISO 34-1 | kN/m | 126 |
| Strength at 100 % strain xy-direction | DIN 53504 (200 mm/min) | MPa | 12 |
Downloads
-
Technical Data Sheet
-
Safety Data SheetNo direct download available, please visit www.productsafetyfirst.covestro.com