Addigy® GPU 77D 000000 X1010
Additive manufacturing Thermoplastic Polyurethane grade for filament extrusion. Aromatic ether-based type; tough and rigid; transparent.
i
Market Switch
Selection will influence the results you get.
About
Product Types
- TPU
Material
- 3D Print
- Good surface finish, Good adhesion to printing bed, Good layer adhesion, Easy printable
- Foams
- Rigid
- Thermoplastic Polyurethane
- Transparent
General Characterization
No data available
Storage Conditions
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Vicat softening temperature 10 N, 50 °C/h | ISO 306 | °C | 133 |
| Abrasion resistance | ISO 4649 method A | mm^3 | 52 |
| Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 440 |
| Density | ISO 1183-1 | kg/m^3 | 1190 |
| Tensile strength z-direction | ISO 527-2 (200 mm/min) | MPa | 13 |
| Young’s Modulus z-direction | ISO 527-2(1 mm/min) | MPa | 370 |
| Elongation at break z-direction | ISO 527-2 (200 mm/min) | % | 18 |
| Shore hardness D | DIN ISO 7619-1 (1s) | 77 | |
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 280 |
| Tensile strength xy-direction | ISO 527-2 (200 mm/min) | MPa | 27 |
| Appearance | natural color |