Addigy® GPC 3D1000C 000000
Additive manufacturing Polycarbonate grade for filament extrusion. Transparent, tough and rigid; easy processing, low viscosity
i
Market Switch
Selection will influence the results you get.
About
Product Types
- Polycarbonate
Material
- Coatings, paints & inks
- Low viscous
- 3D Print
- Good surface finish, Good layer adhesion, Low warping, Easy printable
- Plastics
- Transparent
- Foams
- Rigid
General Characterization
No data available
Storage Conditions
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Appearance | natural color | ||
| Elongation at break xy-direction | ISO 527-2(1 mm/min) | % | 4 |
| Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 63 |
| Melt volume rate 300 °C; 1.2 kg | ISO 1133 | cm^3 / 10 min | 34 |
| Density | ISO 1183-1 | kg/m^3 | 1210 |
| Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 2010 |
| Impact strength yz-directionCharpy unnotched | ISO 179-1 | kJ/m^2 | 64 |
| Vicat softening temperature 50 N; 50 °C/h | ISO 306 | °C | 112 |