Addigy® GPC 3052RC 000000
Additive manufacturing Polycarbonate grade for filament extrusion. Recycled grade made from pre-consumer material. High viscous, high strength, transparent.
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Tensile strength z-direction | ISO 527-2(200 mm/min) | MPa | 53 |
| Elongation at break z-direction | % | 5 | |
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 27 |
| Vicat softening temperature 50 N; 50 °C/h | ISO 306 | °C | 149 |
| Young’s Modulus z-direction | ISO 527-2(1 mm/min) | MPa | 1940 |
| Density | ISO 1183-1 | kg/m^3 | 1220 |
| Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 2070 |
| Impact strength xy-direction | ISO 180/1U | kJ/m^2 | 185 |
| Impact strength xz-direction | ISO 180/1U | kJ/m^2 | 178 |
| Appearance | natural color | ||
| Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 60 |
| Glass transition temperature | DIN EN ISO 11357-1 | °C | 150 - 153 |
| Melt volume rate 300 °C; 1.2 kg | ISO 1133 | cm^3 / 10 min | 6.5 - 7.5 |