Addigy® FPB 2684 000000 A
Additive manufacturing Polycarbonate blend for filament extrusion. Diameter: 1.75 mm Tough and rigid, heat resistant, cold stable, UV stable; easy processing. Natural color.
i
Market Switch
Selection will influence the results you get.
About
Product Types
No data available
Material
No data available
General Characterization
No data available
Storage Conditions
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
Sampling
No data available
Packaging Type
No data available
Technical Properties & Datasheets
Specifications
| Property Name | Test Method | Unit | Value |
|---|---|---|---|
| Volume Resistivity | IEC 60093 | Ohm m | 10^14 |
| Vicat softening temperature 50 N; 120 °C/h | ISO 306 | °C | 120 |
| Density | ISO 1183-1 | kg/m^3 | 1130 |
| Impact strength z-direction | ISO 180/1U | kJ/m^2 | 2.12 |
| Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 47 |
| Appearance | natural color | ||
| Heat deflection temperature 1.82 MPa | ASTM D 648 | °C | 110 |
| Young’s Modulus xy-direction | ISO 527-2 (1 mm/min) | MPa | 1930 |
| Tensile strength z-direction | ISO 527-2 (200 mm/min) | MPa | 28 |
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 12 |
| Heat deflection temperature 0.45 MPa | ASTM D 648 | °C | 130 |
| Elongation at break z-direction | ISO 527-2 (200 mm/min) | % | 1.7 |
| Young’s Modulus z-direction | ISO 527-2 (1 mm/min) | MPa | 1990 |
| Melt volume rate 300 °C; 1.2 kg | ISO 1133 | cm^3 / 10 min | 18 |
| Impact strength xy-direction | ISO 180/1U | 104 |