Addigy® LPU Flex 341-10 IM

Clear aliphatic polyether urethane acrylate resin specifically developed for 3D printing applications requiring high mechanical flexibility. By using it as a primary component in 3D printing formulations, the mechanical properties of the final printed parts can tuned in a wide range to meet the required specifications. This versatile resin is compatible with a variety of reactive thinners, mixable with other Addigy® LPU products, and can be used in 1- or 2-component based formulations in combination with isocyanate reactive compounds.

Kontaktieren Sie einen Experten
i
Markt wechseln
Die Auswahl beeinflusst die Ihnen angezeigten Ergebnisse.
In die Zwischenablage kopiert

Über

Materialklassen

  • Prepolymer
  • Prepolymer
  • PU-Harze

Material

3D Druck
Compatible with a variety of reactive thinners
Lacke
flexibel

Allgemeine Charakterisierung

Clear aliphatic polyether urethane acrylate resin specifically developed for 3D printing applications requiring high mechanical flexibility.
By using it as a primary component in 3D printing formulations, the mechanical properties of the final printed parts can tuned in a wide range to meet the required specifications.
This versatile resin is compatible with a variety of reactive thinners, mixable with other Addigy® LPU products, and can be used in 1- or 2-component based formulations in combination with isocyanate reactive compounds.

Lagerungsbedingungen

- Storage in original sealed Covestro container.
- Recommended storage temperature: 10 - 30 °C.
- Keep container dry and tightly closed in a cool and well ventilated place.
- Protect against heat and direct sunlight.

Probenahme

Keine Daten verfügbar

Verpackungsart

Keine Daten verfügbar

Technische Eigenschaften & Datenblätter

Name der Eigenschaft Prüfverfahren Einheit Wert
Appearance clear
Double bond density % 6.2
NCO (blocked) % 3.7
Viscosity at 23 °C DIN EN ISO 3219 mPa s 10,000 - 16,000
Density at 23 °C DIN EN ISO 2811-3 g/cm^3 1.05
Color DIN EN 1557 Hazen 7 - 17

Name der Eigenschaft Prüfverfahren Einheit Wert
Glass transition temperature DIN EN ISO 6721-1 °C 70
Elongation at break xy-direction ISO 527-2(200 mm/min) % 118
Young’s Modulus xy-direction ISO 527-2(1 mm/min) MPa 100
Tensile strength at break xy-direction ISO 527-2(200 mm/min) MPa 24

Downloads

Technisches Datenblatt
Sicherheitsdatenblatt
Kein direkter Download verfügbar, bitte besuchen Sie www.productsafetyfirst.covestro.com
Download

Möchten Sie mehr über Addigy® LPU Flex 341-10 IM erfahren?
Setzen Sie sich mit unseren Experten in Verbindung!

Contact form image Zoe

Wie können wir Sie kontaktieren?

* Pflichtfelder

Compare