Addigy® FPB 2684 901510 B
Additive manufacturing Polycarbonate blend for filament extrusion. Diameter: 2.85 mm Tough and rigid, heat resistant, cold stable, UV stable; easy processing. Black color.
i
Markt wechseln
Die Auswahl beeinflusst die Ihnen angezeigten Ergebnisse.
Über
Materialklassen
Keine Daten verfügbar
Material
Keine Daten verfügbar
Allgemeine Charakterisierung
Keine Daten verfügbar
Lagerungsbedingungen
The product should be stored in its original packaging at all times.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
If bags or containers have been opened, they must then be sealed again to ensure proper further storage.
Prolonged exposure of bags or containers containing Addigy® filaments or pellets to light or light sources containing UV rays should be avoided. UV radiation will lead to degradation especially, but not limited color changes of the filaments or pellets and subsequently molded parts.
Constant, normal room temperature with minimal fluctuations and low to normal humidity is essential.
It is important to properly dry the filaments and pellets, as directed for the product, prior to processing.
Probenahme
Keine Daten verfügbar
Verpackungsart
Keine Daten verfügbar
Technische Eigenschaften & Datenblätter
Genannte Eigenschaften Spezifikation
| Name der Eigenschaft | Prüfverfahren | Einheit | Wert |
|---|---|---|---|
| Vicat softening temperature 50 N; 120 °C/h | ISO 306 | °C | 120 |
| Heat deflection temperature 1.82 MPa | ASTM D 648 | °C | 110 |
| Density | ISO 1183-1 | kg/m^3 | 1130 |
| Melt volume rate 300 °C; 1.2 kg | ISO 1133 | cm^3 / 10 min | 18 |
| Tensile strength xy-direction | ISO 527-2(200 mm/min) | MPa | 47 |
| Appearance | black | ||
| Young’s Modulus xy-direction | ISO 527-2(1 mm/min) | MPa | 1930 |
| Elongation at break xy-direction | ISO 527-2(200 mm/min) | % | 12 |
| Volume Resistivity | IEC 60093 | Ohm m | 10^14 |
| Impact strength xy-direction | ISO 180/1U | kJ/m^2 | 190 |
| Heat deflection temperature 0.45 MPa | ASTM D 648 | °C | 130 |
Downloads
-
Technisches Datenblatt
-
SicherheitsdatenblattKein direkter Download verfügbar, bitte besuchen Sie www.productsafetyfirst.covestro.com